PLA Ultralight

Outside the US or Canada?
Click HERE

Clear

Description

Compatibility:

 

 

PLA Ultralight (Poly-Lactic Acid) is a a general-use bio performance thermoplastic for open-environment 3D printing. It’s a filament with an open cell structure that results in a spongy texture when printed. Due to this quality, layers are barely visible on the smooth printed surface and the material can be easily sanded, cut, and otherwise shaped as needed. Uniquely, the material prints with vastly altered material properties depending on the print conditions. At higher temperatures with a lower throughput, the most lightweight foam is produced. On standard PLA settings, the material is tough and impact resistant. It features a density of approximately 50-60% of a part printed with standard PLA.

Best suited for lightweight objects, shock-absorbent supports, or parts that require malleability, such as in forms and moulding or modeling and prototyping applications. But be aware, to find the best foam/solid balance for your part, you need to be willing to tweak and tune some settings.

Highlights:

  • 50-60% lighter than standard PLA
  • Easily malleable for post processing
  • Variable weight and strength potential
  • Sustainable bio polymer
  • Needs experimental mindset *

*to design and print with the best suitable foam/solid composition part

Please contact us at “applications[at]bigrep.com” for further support with PLA Ultralight

Specifications

PHYSICAL PROPERTIES

Material Polylactic Acid
Filament Sizes 2.5, 4.5 kg (8.0 kg in prep)
Diameter 2.85 mm
Density ca. 1.0 g/cm³
Flexural Modulus (ISO 178) variable
Tensile Strength (ISO 527) variable
Impact Strength Notched variable kJ/m²
Heat Resistance HDT / B (ISO 75) 40 °C
Hardness (Shore) variable

 

RECOMMENDED PRINTING CONDITIONS

Nozzle Temperature >200 °C
Print Bed Temperature 60 °C
Environmental Temperature n.s. °C
Printing Speed >40 mm/s